Rubber to Metal Bonding Agent

Place of Origin : China
Brand Name : Exceedchem
Certification : ISO90001:2008
Model Number : BA-221
MOQ : 10kg
Price : FOB Qingdao USD10-20/kg
Packaging Details : 3.5kg/drum;17kg/drum
Delivery Time : within two weeks after confirming the order
Payment Terms : TT; LC at sight
Supply Ability : 10tons per year
Contact Now

Heat Vulcanization Bonding Agent BA-221

Metal to Rubber Bonding Agent

(equivalent to Chemlok 220& CILBOND 80ET)

1. Application

BA-221 is a heat vulcanization bonding agent for rubber and various metals.

2. Characteristics

  • It is a high strength bonding agent for unvulcanized rubber and metals coated with BA-213.
  • The applicable rubbers include NR, CR, BR, SBR, PIPR, IIR, EPR, EPDM.
  • It is non-toxic, easily operated.
  • It can be applied with different ways like dip coating, spraying, brushing, and roller coating.
  • It has excellent resistance to heating, water, solvent, oil, salt, corrosion etc.
  • It has high bonding strength, stability and long durability.

3. Physical Properties

  • Component: High polymer, organic compound, inorganic filler and organic solvent.
  • Color: Black
  • Viscosity: (25℃, Brookfield LV2 30rpm) 200-350cps
  • Solid Content: 23-27%
  • Flash Point: 27℃
  • Diluents: Xylene
  • Solvent: Xylene
  • Shelf life: 12 months in unopened containers (25℃)

4. Applying BA-221

  • Surface Preparation: All bonding surface must be contaminant (such as oil, rust, oxide etc) free to reach optimum bonding effects. Surfaces should be grit-blasted, and then ideally degreased. Apply BA-213 and wait it becomes dry.
  • Mixing: Homogeneous mix must be ensured before applying bonding agent.
  • Dilution: Proper quantity dilutes can also be added according to dosage. The diluted bonding agent cannot be stored for long time.
  • Brushing: Unnecessary for dilution
  • Roller coating: 100 portion of BA-221 with 10-15 portion diluents
  • Dipping coating: 100 portion of BA-221 with 10-15 portion diluents
  • Spraying: 100 portion of BA-221 with 50 portion diluents
  • Coating thickness: The coating should be uniform. Drying coating thickness is 15-25 microns.
  • Drying: After applying BA-221, it should be left for 45-60minutes to dry at room temperature. Pre-warming or heating will speed up drying.
  • Storage: It should be stored in dry environment at room temperature. Avoid long time exposure in high humidity and temperature environment.
  • After treatment: Before heating vulcanization, use cloth strip soaked with xylene to clean the excessive bonding agent. Once cured, dilutes cannot clean the bonding agent.
  • Vulcanization: For optimum adhesion effects, rubber and bonding agent should be vulcanized at the same time. When the coated parts are placed in the mould, fill rubber inside and then close the mould to start vulcanization immediately. Recommended vulcanization temperature is 145-185℃. Recommended vulcanization time is 5-60minutes. Vulcanization pressure is according to practical situation.

5. Notes

  • Close the diluents container tightly after use.
  • The diluents vapor is hazardous. Prevent long time inhalation or skin contact in working place.

6. Packing

3.5kg/drum; 17kg/drum

China Customized Inflatable Bumper Ball Game Bubble Adult Grass CE supplier

Rubber to Metal Bonding Agent Images

Inquiry Cart 0
Send your message to this supplier
Enter your email please.
To: Qingdao Exceed Fine Chemicals Co.,Ltd
Characters Remaining: (0/3000)
Inquiry Cart 0